Temperature-Dependent Hall and Field-Effect Mobility in Strongly Coupled All-Inorganic Nanocrystal Arrays

Abstract

We report on the temperature-dependent Hall effect characteristics of nanocrystal (NC) arrays prepared from colloidal InAs NCs capped with metal chalcogenide complex (MCC) ligands (In2Se42- and Cu7S4-). Our study demonstrates that Hall effect measurements are a powerful way of exploring the fundamental properties of NC solids. We found that solution-cast 5.3 nm InAs NC films capped with copper sulfide MCC ligands exhibited high Hall mobility values over 16 cm(2)/(V s). We also showed that the nature of MCC ligands can control doping in NC solids. The comparative study of the temperature-dependent Hall and field-effect mobility values provides valuable insights concerning the charge transport mechanism and points to the transition from a weak to a strong coupling regime in all-inorganic InAs NC solids.우리는 금속 칼코겐화물 콤플렉스 (MCC) 리간드에 싸여 있는 콜로이드성 인아 노스캐롤라이나 주로부터 준비된 나노결정 (노스캐롤라이나 주) 어레이의 온도 의존 홀 효과 특성에 대해 보도한다 (2 세 4 2&ndash에서; 그리고 구리 7 S 4 ? ). 홀 효과 측정이 노스캐롤라이나 주 고체의 기본 특성을 연구하는 강력한 방법이라고 우리의 연구는 증명한다. 구리 황화물 MCC 리간드에 싸여 있는 용액 주조 5.3 나텀 인아 노스캐롤라이나 주 필름이 16 크텀 2 /(V s) 위에서 높은 홀 이동도 값을 나타냈다는 것을 우리는 알았다. 또한 MCC 리간드의 성질이 노스캐롤라이나 주 고체에서 도핑을 제어할 수 있다는 것을 우리는 보여주었다. 온도 의존 홀과 전계 효과 이동성 값에 대한 비교 학습은 약한 것 모든 무기성 InAs 노스캐롤라이나 주 고체에서 강한 레짐 연결까지 전이에 전하 전송 메커니즘과 핵심과 관계가 있는 가치있는 통찰력을 제공한다. 그래픽 요약 ACS 전자적 지지 인포