Permeation barrier properties of an Al2O3/ZrO2 multilayer deposited by remote plasma atomic layer deposition

Title
Permeation barrier properties of an Al2O3/ZrO2 multilayer deposited by remote plasma atomic layer deposition
Other Titles
ZrO2 multilayer deposited by remote plasma atomic layer deposition
Author
전형탁
Keywords
Remote plasma atomic layer deposition; Encapsulation; Al2O3; ZrO2
Issue Date
2014-04
Publisher
Elsevier
Citation
Current Applied Physics,Vol.14 No.4 [2014] ,552-557(6쪽)
Abstract
We report the permeation barrier properties of Al2O3/ZrO2 multi-layers deposited by remote plasma atomic layer deposition. Electrical Ca degradation tests were performed to derive the water vapor transmission rate (WVTR) of Al2O3, ZrO2 and Al2O3/ZrO2 multi-layers at 50 C and 50% relative humidity (RH). Al2O3/ZrO2 multi-layers exhibit better barrier properties than Al2O3 and ZrO2 layers, and when more individual layers were deposited in the same total thickness, the WVTR value was reduced further, indicating a better barrier property. The WVTR of the Al2O3 and ZrO2 layers were 9.5 103 and 1.6 102 g/m2 day, respectively, but when deposited alternatively with 1 cycle of each layer, the WVTR decreased to 9.9 104 g/m2 day. X-ray diffraction results indicated that ZrO2 has a monoclinic structure but Al2O3 and Al2O3/ZrO2 multi-layers show an amorphous structure. Cross sectional Al2O3/ZrO2 multilayer structures and the formation of a ZrAlxOy phase are observed by transmission electron microscopy (TEM). X-ray photoelectron spectrometry (XPS) results indicate that Al2O3 and ZrO2 contain 33.7% and 37.8%, respectively, AleOH and ZreOH bonding. However, the ZrAlxOy phase contained 30.5% AleOH and ZreOH bonding. The results of transmittance measurement indicate that overall, Al2O3, ZrO2 and Al2O3/ ZrO2 multi-layers show high transmittance greater than 80% in the visible region. We report the permeation barrier properties of Al"2O"3/ZrO"2 multi-layers deposited by remote plasma atomic layer deposition. Electrical Ca degradation tests were performed to derive the water vapor transmission rate (WVTR) of Al"2O"3, ZrO"2 and Al"2O"3/ZrO"2 multi-layers at 50 ^oC and 50% relative humidity (RH). Al"2O"3/ZrO"2 multi-layers exhibit better barrier properties than Al"2O"3 and ZrO"2 layers, and when more individual layers were deposited in the same total thickness, the WVTR value was reduced further, indicating a better barrier property. The WVTR of the Al"2O"3 and ZrO"2 layers were 9.5 x 10^-^3 and 1.6 x 10^-^2 g/m^2 day, respectively, but when deposited alternatively with 1 cycle of each layer, the WVTR decreased to 9.9 x 10^-^4 g/m^2 day. X-ray diffraction results indicated that ZrO"2 has a monoclinic structure but Al"2O"3 and Al"2O"3/ZrO"2 multi-layers show an amorphous structure. Cross sectional Al"2O"3/ZrO"2 multi-layer structures and the formation of a ZrAl"xO"y phase are observed by transmission electron microscopy (TEM). X-ray photoelectron spectrometry (XPS) results indicate that Al"2O"3 and ZrO"2 contain 33.7% and 37.8%, respectively, Al-OH and Zr-OH bonding. However, the ZrAl"xO"y phase contained 30.5% Al-OH and Zr-OH bonding. The results of transmittance measurement indicate that overall, Al"2O"3, ZrO"2 and Al"2O"3/ZrO"2 multi-layers show high transmittance greater than 80% in the visible region.
URI
https://www.kci.go.kr/kciportal/ci/sereArticleSearch/ciSereArtiView.kci?sereArticleSearchBean.artiId=ART001875181http://hdl.handle.net/20.500.11754/51347
ISSN
1567-1739; 1878-1675
DOI
10.1016/j.cap.2013.11.053
Appears in Collections:
COLLEGE OF ENGINEERING[S](공과대학) > MATERIALS SCIENCE AND ENGINEERING(신소재공학부) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE