Improving wear resistance of cBN-based cutting tools using TiN coating on cBN powder surface
- Title
- Improving wear resistance of cBN-based cutting tools using TiN coating on cBN powder surface
- Author
- 신동욱
- Keywords
- Cubic boron nitride; Liquid phase deposition; Cutting tools
- Issue Date
- 2021-12
- Publisher
- ELSEVIER
- Citation
- COLLOIDS AND SURFACES A-PHYSICOCHEMICAL AND ENGINEERING ASPECTS, v. 631, article no. 127758, Page. 1-5
- Abstract
- TiN-coated cBN was successfully synthesized using the liquid phase deposition method with TiF4 as the Ti source. The crystal phase of the TiOx coating layer was transformed into Ti4O7 and TiN via sintering under a reduction atmosphere in a vacuum furnace. It was then completely converted to the TiN phase at a sintering temperature of 1200 °C. The coating layers exhibited a uniform thickness of approximately 20–40 nm, regardless of the sintering temperature. PcBN cutting tools prepared using the cBN@TiN powders showed excellent wear resistance under heavy cutting conditions; delivering an average machining distance of 10,766 m and a flank wear width of 0.3 mm in 108 min. This wear resistance is approximately four times that of a cutting tool manufactured using cBN powder.
- URI
- https://www.sciencedirect.com/science/article/pii/S0927775721016277?via%3Dihubhttps://repository.hanyang.ac.kr/handle/20.500.11754/178219
- ISSN
- 0927-7757;1873-4359
- DOI
- 10.1016/j.colsurfa.2021.127758
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > MATERIALS SCIENCE AND ENGINEERING(신소재공학부) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML