미소접합시험과 유한요소법을 통한 섬유/에폭시 복합재의 계면 전단강도 해석

Abstract

Interfacial shear strength between epoxy and carbon fiber has been analyzed utilizing the microbond specimen with an epoxy micro-droplet adhered onto single carbon fiber. The interfacial shear stress distributions along the fiber/matrix interface were calculated by finite element analysis using three kinds of finite element models such as droplet model, circular-crosssection model and pull-out model. Conclusions were obtained as follows. (1) Interfacial shear stress distribution showed that larger stresses were concentrated in the fiber/matrix interface for microbond test than for pull-out test. Thus, debonding at the fiber/matrix interface during microbond test was liable to occur at low load level. (2) Microbond test showed higher interfacial strength which was caused by various effects of micro-droplet geometry and size as well as stress concentration in the region contacting with the micro-vise tip. 미소 드랍릿 시편을 이용한 탄소섬유와 에폭시 수지 사이의 계면전단강도에 대해 시험분석하였다. 또한 드랍릿 모델, 원형단면 모델, 인발모델의 3종류의 유한요소해석을 통해 섬유/수지간의 응력분포를 계산하였다. 본 연구결과는 다음과 같다. (1) 미소드랍릿 시험의 경우는 인발시험보다 섬유/수지의 계면에서 큰 응력집중이 나타났으며 계면박리가 낮은 하중수준에서도 발생하기 용이함을 알수 있었다. (2) 미소드랍릿시험에서 높은 계면강도를 보였는데, 이는 미소드랍릿의 형상과 사이즈, 바이스팁과 접촉하는 부위의 응력집중효과를 함께 받았기 때문으로 해석되었다.