Thermal and Physical Properties of Oligo-(propylene oxide-block-ethylene oxide) Allyl Methyl Ether Containing Tetrasiloxane as Wetting Agent
- Title
- Thermal and Physical Properties of Oligo-(propylene oxide-block-ethylene oxide) Allyl Methyl Ether Containing Tetrasiloxane as Wetting Agent
- Author
- 노시태
- Keywords
- wetting agents; OA-oligo(PO-b-EO)Me series; inorganic electrolyte; hydrolysis; siloxane backbone
- Issue Date
- 2003-09
- Publisher
- 한국공업화학회
- Citation
- Journal of Industrial and Engineering Chemistry, v. 9, no. 5, page. 526-536
- Abstract
- Polydisperse oligo(propylene oxide-block-ethylene oxide) allyl methyl ether tetrasiloxane wetting agents [OA-oligo(PO-b-EO)Me series] were synthesized by hydrosilylation reaction of OMTS and allyl-oligo(PO-b-EO)Me series. Weight loss temperature and Tps of OA-oligo(EO)Me series were increased due to the increase of EO chain length. When PO ratio was increased, Tps of OA-oligo(PO-b-EO)Me series was decreased. However, weight loss temperature tended to increase according to the increase of PO ratio. Surface tension and wetting power of OA-oligo(EO)Me series were increased according to the increase of EO chain length. When PO ratio was increased, surface tension and wetting power of OA-oligo(PO-b-EO)Me series were decreased. As inorganic electrolyte was added, surface tension and sedimentation time of aqueous solutions tended to decrease due to the arrangement of surfactant molecules. Also, surface tension and sedimentation time of aqueous solutions were increased at pH 3 and 11 because of the hydrolysis of siloxane backbone.
- URI
- https://www.cheric.org/research/tech/periodicals/view.php?seq=426720https://repository.hanyang.ac.kr/handle/20.500.11754/156198
- ISSN
- 1226-086X
- Appears in Collections:
- COLLEGE OF ENGINEERING SCIENCES[E](공학대학) > MATERIALS SCIENCE AND CHEMICAL ENGINEERING(재료화학공학과) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML