Hot corrosion behaviour of nickel-cobalt-based alloys in a lithium molten salt
- Title
- Hot corrosion behaviour of nickel-cobalt-based alloys in a lithium molten salt
- Author
- 김용수
- Keywords
- Hot corrosion; Ni,Co-based alloy; Lithium molten salt; Electrolytic reduction; Structural material
- Issue Date
- 2019-05
- Publisher
- PERGAMON-ELSEVIER SCIENCE LTD
- Citation
- CORROSION SCIENCE, v. 151, Page. 20-26
- Abstract
- In this study, hot corrosion behaviours of Haynes 282 (H282), Nimonic 90 (N90), and Haynes HR160 (HR160) in LiCI-Li2O molten salt were investigated at 650 degrees C under argon atmosphere. The corrosion rate was in the order of H282 ˂ N90 ˂ HR160, depending on the morphology and structure of the scale. H282 showed a localised corrosion behaviour, while N90 showed a uniform corrosion behaviour. For HR-160, intergranular corrosion was observed. The high Cr content caused intergranular corrosion in the corrosion layer. Thus, excess Cr has a deleterious effect on the corrosion kinetics during hot corrosion in LiCI-Li2O molten salt.
- URI
- https://www.sciencedirect.com/science/article/pii/S0010938X18310199?via%3Dihubhttps://repository.hanyang.ac.kr/handle/20.500.11754/151212
- ISSN
- 0010-938X; 1879-0496
- DOI
- 10.1016/j.corsci.2019.01.041
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > NUCLEAR ENGINEERING(원자력공학과) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML