Flexible nonvolatile memory devices based on Au/PMMA nanocomposites deposited on PEDOT:PSS/Ag nanowire hybrid electrodes
- Title
- Flexible nonvolatile memory devices based on Au/PMMA nanocomposites deposited on PEDOT:PSS/Ag nanowire hybrid electrodes
- Author
- 김태환
- Keywords
- PEDOT:PSS/AgNW; Flexible NVM; Nanocomposite; Electrical characteristic
- Issue Date
- 2017-07
- Publisher
- ELSEVIER SCIENCE BV
- Citation
- APPLIED SURFACE SCIENCE, v. 411, page. 67-72
- Abstract
- Flexible nonvolatile memory (NVM) devices fabricated utilizing Au nanoparticles (AuNPs) embedded in a poly(methylmethacrylate) (PMMA) layer were fabricated on a silver nanowire (AgNW) or a poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS)/AgNW coated on poly(ethylene terephthalate) (PET) substrates. The transmittance and the sheet resistance of the PEDOT:PSS/AgNW hybrid layer were approximately 89% and 50 Omega/sq, respectively, which were comparable to the values for commercial indium-tin-oxide (ITO) electrodes. Current-voltage curves for the Al/PMMA:AuNP/PEDOT:PSS/AgNW/PET devices at 300 K showed clockwise current hysteresis behaviors due to the existence of the AuNPs. The endurance number of ON/OFF switching for the NVM devices was above 30 cycles. An ON/OFF ratio of 1 x 10(3) was maintained for retention times longer than 1 x 10(4) s. The maximum memory margins of the NVM devices before and after bending were approximately 3.4 x 10(3) and 1.4 x 10(3), respectively. The retention times of the devices before and after bending remained same 1 x 10(4) s. The memory margin and the stability of flexible NVMs fabricated on AgNW electrodes were enhanced due to the embedded PEDOT:PSS buffer layer. (C) 2017 Elsevier B.V. All rights reserved.
- URI
- https://www.sciencedirect.com/science/article/pii/S0169433217307717?via%3Dihubhttps://repository.hanyang.ac.kr/handle/20.500.11754/114719
- ISSN
- 0169-4332; 1873-5584
- DOI
- 10.1016/j.apsusc.2017.03.112
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > ELECTRONIC ENGINEERING(융합전자공학부) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML