Electrodeposited NiAl-layered double hydroxide on Co3O4 as binder-free electrode for supercapacitor
- Title
- Electrodeposited NiAl-layered double hydroxide on Co3O4 as binder-free electrode for supercapacitor
- Author
- 형우치
- Advisor(s)
- Erfan Zal Nezhad
- Issue Date
- 2018-08
- Publisher
- 한양대학교
- Degree
- Master
- Abstract
- In this study, constant-voltage, NiAl-layered double hydroxide (LDH) nanosheet arrays (NSAs) were successfully grown on Co3O4 nanowires as binder-free electrode for a supercapacitor. LDH nanosheets with a large active surface area evenly dispersed on the surface of Co3O4 nanowires to achieve fast electron transport and improve the electrochemical properties of LDH nanosheets. A high specific capacitance of 2010.91 F g−1 was exhibited at a current density of 2 A g−1, and the specific capacitance of the Co3O4@NiAl-LDH remained as high as 1454.55 F g−1 at a high current density of 40 A g−1 with a retention rate of 72.3%. An asymmetric supercapacitor (ASC) was fabricated using Co3O4 @ LDH nanosheets as the positive electrode and CNT as the negative electrode. The ASC exhibited a high energy density of 12.6 Wh kg−1, and the corresponding power density was 401.4 W kg−1. Through various experiments, it can be concluded that electrodeposited LDH nanosheets on Co3O4 nanowires show good potential as a supercapacitor electrode material.
- URI
- https://repository.hanyang.ac.kr/handle/20.500.11754/75787http://hanyang.dcollection.net/common/orgView/200000433366
- Appears in Collections:
- GRADUATE SCHOOL[S](대학원) > MECHANICAL CONVERGENCE ENGINEERING(융합기계공학과) > Theses (Master)
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML