Influence of Cr on Weld Solidification Cracking in Fe-15Mn-0.5C-3.5Al-xCr Alloys
- Title
- Influence of Cr on Weld Solidification Cracking in Fe-15Mn-0.5C-3.5Al-xCr Alloys
- Author
- 이창희
- Keywords
- solidification cracking; high Mn steel; welding; solidification; eutectic
- Issue Date
- 2015-01
- Publisher
- IRON STEEL INST JAPAN KEIDANREN KAIKAN
- Citation
- ISIJ INTERNATIONAL, v. 55, NO 1, Page. 257-263
- Abstract
- The solidification cracking sensitivity of Fe-15Mn-0.5C-3.5Al-xCr (x = 5, 12 mass%) alloys was evaluated using a longitudinal Varestraint test and compared with that of austenitic Fe-18Mn-0.6C alloy. Weld microstructures of Low Cr (5 mass%) and High Cr (12 mass%) alloys revealed duplex structures with a mixture of austenite and delta ferrite. The amounts of residual delta ferrite and (Cr, Fe, Mn)(23)C-6 carbide remarkably increased with increasing Cr content. A small amount of Cr addition (5 mass%) provided negligible influence on the solidification cracking susceptibility. However, the welds of high Cr alloys demonstrated excellent resistance to solidification cracking due to healing by the eutectic liquid. The addition of Cr enhanced the formation of a low melting point (gamma + (Cr, Fe,Mn)(7)C-3) eutectic during solidification by increasing the eutectic formation temperature and simultaneously decreasing the eutectic C content.
- URI
- http://hdl.handle.net/20.500.11754/21344https://www.jstage.jst.go.jp/article/isijinternational/55/1/55_257/_article
- ISSN
- 0915-1559
- DOI
- 10.2355/isijinternational.55.257
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > MATERIALS SCIENCE AND ENGINEERING(신소재공학부) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML