dc.description.abstract | The effect of surface treatment of carbon fiber reinforced plastic (CFRP) composites on the T-peel strength and the shear strength between CFRP and aluminum panels was studied. The surface of the composite panel was treated with Ar+ irradiation under oxygen environment. The optimal Ar+ ion dose was determined by measuring the changes of contact angle and surface energy as a function of ion dose. T-peel tests and SLS tests were performed using irradiated CFRP/aluminum specimens and unirradiated CFRP/aluminum specimens to determine the treatment effect by Ar+ irradiation under oxygen environment on the T-peel strength and shear strength of CFRP/aluminum composites. The results showed that contact angle on the surface of the composite panel was reduced from ∼80° to ∼8° and the surface energy increased from 31 ergs/cm2 to 72.4 ergs/cm2 with an ion dose of 1017 ions/cm2. T-peel strength and shear strength are significantly affected by the surface treatment of composite panel. T-peel strength and shear strength improved 650% and 56%, respectively, when the treatment was made with an ion dose of 1016 ions/cm2. SEM examination showed that the improvement of bonding strength was attributed to the uniform spread and fracture of epoxy adhesive. | en_US |
dc.language.iso | en_US | en_US |
dc.publisher | SOC PLASTICS ENG INC | en_US |
dc.title | Surface Treatment of CFRP Composites by Ar+ Irradiation to Improve Bonding Strength between Aluminum and CFRP Composites | en_US |
dc.type | Article | en_US |
dc.identifier.doi | 10.1002/pc.10508 | - |
dc.relation.journal | POLYMER COMPOSITES | - |
dc.contributor.googleauthor | Rhee, K.Y. | - |
dc.contributor.googleauthor | Choi, N.-S. | - |
dc.contributor.googleauthor | Park, S.-J. | - |
dc.relation.code | 2009207746 | - |
dc.sector.campus | E | - |
dc.sector.daehak | COLLEGE OF ENGINEERING SCIENCES[E] | - |
dc.sector.department | DEPARTMENT OF MECHANICAL ENGINEERING | - |
dc.identifier.pid | nschoi | - |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.