열분해법과 레이저 어블레이션을 이용한 질소 도핑된 기능성 TiO2 나노입자의 제조
- Title
- 열분해법과 레이저 어블레이션을 이용한 질소 도핑된 기능성 TiO2 나노입자의 제조
- Other Titles
- Fabrication of functional N-doped TiO2 nanoparticles by thermal decomposition method and laser ablation
- Author
- 구현진
- Alternative Author(s)
- Koo, Hyun Jin
- Advisor(s)
- 심광보
- Issue Date
- 2010-02
- Publisher
- 한양대학교
- Degree
- Master
- Abstract
- In order to utilize visible light in photocatalytic reactions, nitrogen atoms were doped in photocatalytic TiO2 powders using an organic compound such as guanidine hydrochloride and guanidine carbonate. The visible light induced photo absorption effect of the as-prepared 2M Gua-HCl condition sample was much higher than other conditions. Optimum sintering condition of TiO2(anatase) target for PLA in liquid was obtained at 800 ℃ (rising ration was 5 ℃ /min) for 20h.. A Nd:YAG nanosecond laser (30 Hz, 355 nm) was used for PLA process in liquid. To obtain TiO2-xNx nanocolloids(40-60nm) with anatase and rutile phase mixed, the target was irradiated at 48 mJ/cm2 for 2hr in ethanol (20ml). Well dispersed TiO2-xNx@PPy core/shell nanoparticles, oxidized by laser irradiation process, were simply obtained.
- URI
- https://repository.hanyang.ac.kr/handle/20.500.11754/142764http://hanyang.dcollection.net/common/orgView/200000413981
- Appears in Collections:
- GRADUATE SCHOOL[S](대학원) > MATERIALS SCIENCE & ENGINEERING(신소재공학과) > Theses (Master)
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML