전압, pH변화에 따른 철나노튜브의 형상변화 예측
- Title
- 전압, pH변화에 따른 철나노튜브의 형상변화 예측
- Other Titles
- Iron Nanotube's Morphorlogy by Changing Voltage and pH
- Author
- 박재우
- Keywords
- Anodization; Fenton process; Iron nanotube; Morphorlogy
- Issue Date
- 2011-06
- Publisher
- 한국지반환경공학회
- Citation
- 지반환경, 2011, 12(2), P.45-56(12)
- Abstract
- Fenton and photo-Fenton processes have been proven to be effective methods to treat organic pollutants. Although, Fenton precesses are regareded as a kind of powerful methods. The pH range suitable for reacting is very narrow, and it is costly to remove the iron ions from system after the reaction was over. Thus, many works have been focused on the heterogeneous Fenton process to avoid the disadvantages mentioned above. In this research, we reported the synthesis of self-organized nanoporous iron film treated with anodization and electro-reduction of iron foil under variable pH and voltage. The iron nanotubes were fabricated in 1M Na₂SO₄ + 0.25wt% NaF electrolyte. The morphorlogy of iron nanotube was characterized by field emission scanning electron microscope(FESEM) and The crystalline structures of fabricated film were evaluated using X-ray diffraction(XRD).
- URI
- http://www.dbpia.co.kr/Journal/ArticleDetail/NODE01560575
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > CIVIL AND ENVIRONMENTAL ENGINEERING(건설환경공학과) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML