Corrigendum to “Self-organized TiO2 nanotube layer on Ti–6Al–7Nb for biomedical application” [SCT 265C (2015) Pages 24–31]

Title
Corrigendum to “Self-organized TiO2 nanotube layer on Ti–6Al–7Nb for biomedical application” [SCT 265C (2015) Pages 24–31]
Authors
Erfan Zal Nezhad
Issue Date
2015-03
Publisher
ELSEVIER SCIENCE SA
Citation
SURFACE & COATINGS TECHNOLOGY, v. 272, Page. 428-428
Abstract
In the present study, a self-organized nanotube TiO2 layer on Ti–6Al–7Nb was fabricated. The influence of acidic electrolytes including glycerol (G) and ethylene glycol (EG) on the anodization, microstructural features and surface wettability was explored. The phase compositions and morphological characteristics were characterized by X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM), respectively. According to the results, due to the intrinsic amorphous feature of ceramic oxide, the characteristic TiO2 peaks were not detected in the XRD profiles. After annealing in normal atmosphere at 600 °C for 2 h, TiO2 crystallized and consequently, nanotubular TiO2 arrays containing anatase and rutile phases formed. From a microstructural point of view, the average length and diameter of the nanotube array ranged from 2.23 to 4.22 μm and 160 to 170 nm, respectively. Besides, the type of acidic electrolyte and subsequent annealing noticeably affected the surface wettability of the products.
URI
http://www.sciencedirect.com/science/article/pii/S0257897215003382http://hdl.handle.net/20.500.11754/22824
ISSN
0257-8972
DOI
http://dx.doi.org/10.1016/j.surfcoat.2015.04.015
Appears in Collections:
COLLEGE OF ENGINEERING[S](공과대학) > MECHANICAL ENGINEERING(기계공학부) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE