Tuning properties of SnO2/Au/SnO(2)multilayer with variable Au thicknesses as transparent conductive oxides
- Title
- Tuning properties of SnO2/Au/SnO(2)multilayer with variable Au thicknesses as transparent conductive oxides
- Author
- 전형탁
- Keywords
- Transparent conducting oxide; Atomic layer deposition; Tin Oxide
- Issue Date
- 2020-09
- Publisher
- IOP PUBLISHING LTD
- Citation
- JAPANESE JOURNAL OF APPLIED PHYSICS, v. 59, no. 10, article no. 105502
- Abstract
- Multilayer tin oxide/gold/tin oxide (SnO2/Au/SnO2) was deposited by atomic layer deposition and an e-beam evaporator. The structural, electrical, and optical properties of the SnO2/Au/SnO(2)multilayer were investigated. Au formed islands at a thickness less than 3 nm. As the Au interlayer thickness increased, the Au islands merged, resulting in a continuous film 12 nm thick. As the Au interlayer thickness increased from 0 to 12 nm, the carrier concentration and Hall mobility increased to 2.41 x 10(22) cm(-3)and 11.96 cm(2) V-1 s(-1), respectively. As a result, the resistivity decreased at 10(-5)ohm cm with an increasing Au interlayer thickness compared to a SnO(2)single layer. In addition, optical transmittance at 550 nm increased by more than 80% at 6 and 9 nm than at Au thicknesses of 3 and 12 nm. SnO2/Au/SnO(2)multilayers are promising candidates as an indium-free transparent conducting oxide for use in high performance optoelectronic devices.
- URI
- https://iopscience.iop.org/article/10.35848/1347-4065/abb4a8https://repository.hanyang.ac.kr/handle/20.500.11754/170661
- ISSN
- 0021-4922; 1347-4065
- DOI
- 10.35848/1347-4065/abb4a8
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > MATERIALS SCIENCE AND ENGINEERING(신소재공학부) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML