High Performance MoSe2/Mo Counter Electrodes Based-Dye-Sensitized Solar Cells
- Title
- High Performance MoSe2/Mo Counter Electrodes Based-Dye-Sensitized Solar Cells
- Author
- 김학성
- Keywords
- counter electrodes; DSSC; MoSe2; Sputtering; transition metal chalcogenides
- Issue Date
- 2017-03
- Publisher
- ELECTROCHEMICAL SOC INC
- Citation
- JOURNAL OF THE ELECTROCHEMICAL SOCIETY, v. 164, no. 2, page. E11-E16
- Abstract
- In the present study, multilayer MoSe2/Mo nanostructures fabricated by surface selenization of Mo-coated glass substrates using magnetron sputtering, was proposed as a counter electrode (CE) catalyst in dye-sensitized solar cells (DSSCs) to speed up the reduction of triiodide I-3(-) to iodide I-. The extensive cyclic voltammograms (CV) and Tafel curve analysis indicated that the current density of the optimized MoSe2/Mo CE was higher than Pt CEs due to the fast reduction species. Furthermore, the peak current densities of theMoSe(2)/Mo CE showed little degradation after consecutive 100 CV cycles, suggesting high electrochemical stability of the MoSe2/Mo CE. In addition, MoSe2/Mo CE exhibited lower charge-transfer resistance than Pt CEs. Finally, the DSSC assembled with the MoSe2/Mo CE showed a high power conversion efficiency of 9.57% under illumination of 100 mW.cm(-2) (DSSC with Pt CE: 9.15%). (C) 2017 The Electrochemical Society. All rights reserved.
- URI
- http://jes.ecsdl.org/content/164/2/E11https://repository.hanyang.ac.kr/handle/20.500.11754/113351
- ISSN
- 0013-4651; 1945-7111
- DOI
- 10.1149/2.1291702jes
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > MECHANICAL ENGINEERING(기계공학부) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML