Thermodynamic investigation on the formation of inclusions containing MgAl2O4 spinel during 16Cr-14Ni austenitic stainless steel manufacturing processes

Title
Thermodynamic investigation on the formation of inclusions containing MgAl2O4 spinel during 16Cr-14Ni austenitic stainless steel manufacturing processes
Author
박주현
Keywords
thermodynamics; stainless steel; inclusion; spinel; deoxidation; activity; crystallization
Issue Date
2008-01
Publisher
ELSEVIER SCIENCE SA
Citation
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, No. 472, No. 1-2, Page. 43-51
Abstract
The formation mechanism of the inclusions containing the spinel crystals has been developed based on the experimental results for the equilibrium between the Fe-16%Cr-14%Ni stainless steel melts and the inclusions as well as the compositions of the inclusions in the plant samples. In the laboratory experiments, the molar content of alumina in the inclusions linearly increases with increasing content of aluminum according to the theoretical expectation and the composition of the inclusions could be described as a function of the activity of aluminum and silicon. From the analysis of the plant samples, the content of MgO and Al(2)O(3) in the calcium silicate type inclusions continuously increases as the steel melts transfer from AOD converter to LT processes and thus, the spinel phase could be crystallized and grown in the calcium silicate matrix during cooling through tundish to cast slabs. On the other hand, the manganese silicate type inclusions were observed after tapping molten steel to the ladle, and then the MnO and Cr(2)O(3) (and SiO(2)) in the inclusions were reduced by silicon and aluminum through LT to CC mold. The fraction of the inclusions containing spinel crystals at cast slabs was at (Al(2)O(3)) < 20 mass%, while it critically increased at (Al(2)O(3)) > 20 mass%. (c) 2007 Elsevier B.V. All rights reserved.
URI
https://www.sciencedirect.com/science/article/pii/S0921509307004649?via%3Dihubhttps://repository.hanyang.ac.kr/handle/20.500.11754/76688
ISSN
0921-5093
DOI
10.1016/j.msea.2007.03.011
Appears in Collections:
COLLEGE OF ENGINEERING SCIENCES[E](공학대학) > MATERIALS SCIENCE AND CHEMICAL ENGINEERING(재료화학공학과) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE