Effect of cyclic sintering process for NdFeB magnet on microstructure and magnetic properties

Abstract

The fabrication of Nd13Dy2Fe79B6 (at.%) sintered magnets through a cyclic sintering process was demonstrated. The coercivity and temperature coefficient of the cyclic sintered specimens were 2252.8 kA/m and -0.47018%degrees C, respectively. It is believed that the Nd-rich phases have effectively penetrated into the boundary between the Nd2Fe14B grains under the cyclic sintering process. Consequently, the microstructures and shape of the Nd-rich phase were controlled by the cyclic sintering process, resulting in high coercivity and temperature stability. (C) 2012 Elsevier B.V. All rights reserved.