Influence of nano silica on the fresh, hardened and durability properties of self-cleaning white Portland cement mortars
- Title
- Influence of nano silica on the fresh, hardened and durability properties of self-cleaning white Portland cement mortars
- Author
- 유재석
- Keywords
- Nano silica; Nano titanium dioxide; White Portland cement mortars; Mechanical properties; Self-cleaning; Photocatalysis; durability; Chloride penetration; Carbonation
- Issue Date
- 2019-06
- Publisher
- KOREAN ASSOC CRYSTAL GROWTH
- Citation
- JOURNAL OF CERAMIC PROCESSING RESEARCH, v. 20, NO 3, Page. 270-275
- Abstract
- In this study, nano titanium dioxide and nano silica have been added in white Portland cement mortars. The dosage of nano-TiO2 was fixed to 3% while the dosage of nano-SiO2 was varied from 0%-3%. Water/binder ratio was 0.45% and binder/sand ratio was 1:3. The workability, water absorption, compressive and flexural strengths of mortars was measured. The permeability of mortars was measured using Nordest test and the carbonation resistance was measured in a carbonation chamber. The degradation of rhodamine B dye on the surface of mortars was measured after exposure of the white mortars to the ultraviolet light. Addition of nano-SiO2 increased the compressive and flexural strengths of mortars, reduced the water absorption of mortars and resisted the penetration of chloride ions. The self-cleaning of the white mortars was unaffected by the addition of nano-SiO2 particles.
- URI
- https://www.kci.go.kr/kciportal/ci/sereArticleSearch/ciSereArtiView.kci?sereArticleSearchBean.artiId=ART002478327http://www.jcpr.or.kr/journal/archive/view/2309https://repository.hanyang.ac.kr/handle/20.500.11754/134139
- ISSN
- 1229-9162; 2672-152X
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > CIVIL AND ENVIRONMENTAL ENGINEERING(건설환경공학과) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML