Defect States in InP/InGaAs/InP Heterostructures by Current-Voltage Characteristics and Deep Level Transient Spectroscopy
- Title
- Defect States in InP/InGaAs/InP Heterostructures by Current-Voltage Characteristics and Deep Level Transient Spectroscopy
- Author
- 김은규
- Keywords
- Metalorganic Chemical Vapor Deposition; InGaAs/InP; Defect States
- Issue Date
- 2018-09
- Publisher
- AMER SCIENTIFIC PUBLISHERS
- Citation
- JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY, v. 18, no. 9, page. 6239-6243
- Abstract
- We studied defect states in In0.53Ga0.47As/InP heterojunctions with interface control by group V atoms during metalorganic chemical vapor (MOCVD) deposition. From deep level transient spectroscopy (DLTS) measurements, two defects with activation energies of 0.28 eV (E1) and 0.15 eV (E2) below the conduction band edge, were observed. The defect density of E1 for In0.53Ga0.47As/InP heterojunctions with an addition of As and P atoms was about 1.5 times higher than that of the heterojunction added P atom only. From the temperature dependence of current-voltage characteristics, the thermal activation energies of In0.53Ga0.47As/InP of heterojunctions were estimated to be 0.27 and 0.25 eV, respectively. It appeared that the reverse light current for In0.53Ga0.47As/InP heterojunction added P atom increased only by illumination of a 940 nm-LED light source. These results imply that only the P addition at the interface can enhance the quality of InGaAs/InP heterojunction.
- URI
- https://www.ingentaconnect.com/content/asp/jnn/2018/00000018/00000009/art00068;jsessionid=4fh1u88nfu7jb.x-ic-live-03https://repository.hanyang.ac.kr/handle/20.500.11754/120103
- ISSN
- 1533-4880; 1533-4899
- DOI
- 10.1166/jnn.2018.15625
- Appears in Collections:
- COLLEGE OF NATURAL SCIENCES[S](자연과학대학) > PHYSICS(물리학과) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML