Microstructural evolution of Al2O3-SiC nanocomposites during spark plasma sinterings

Title
Microstructural evolution of Al2O3-SiC nanocomposites during spark plasma sinterings
Author
좌용호
Keywords
Spark plasma sintering; Al2O3–SiC nanocomposites; Densification behavior; Mechanical properties
Issue Date
2006-03
Publisher
ELSEVIER SCIENCE SA
Citation
JOURNAL OF ALLOYS AND COMPOUNDS, v. 413, No. 1-2, Page. 259-264
Abstract
Al2O3-SiC nanocomposites were fabricated using a spark plasma sintering (SPS) technique, and their densification behavior and mechanical properties were investigated. The rate of densification was higher for the SPS process compared with a conventional hot-pressing process. This enhancement was attributed to an acceleration of the diffusion process due to additional mass-transport mechanisms induced by the spark plasma. Al2O3-SiC nanocomposites were found to possess microstructures of fine SiC particles dispersed within the Al2O3 inatrix grains and/or at the grain boundaries. These nanocomposites (20 vol% SiC) had an average fracture toughness of 3.6 MPa m(1/2) and flexural strength of 812 MPa compared with 2.95 MPa m(1/2) and 663 MPa for the pure Al2O3 compacts, respectively. These increases over the pure matrix have been attributed to the increased rate of densification and to the change in microstructure due to the dispersion of the nano-sized second phase SiC particles. (c) 2005 Elsevier B.V. All rights reserved.
URI
https://www.sciencedirect.com/science/article/pii/S0925838805011898https://repository.hanyang.ac.kr/handle/20.500.11754/110703
ISSN
0925-8388; 1873-4669
DOI
10.1016/j.jallcom.2005.05.049
Appears in Collections:
COLLEGE OF ENGINEERING SCIENCES[E](공학대학) > MATERIALS SCIENCE AND CHEMICAL ENGINEERING(재료화학공학과) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE