The Effect of Temperature on Microstructure, Magnetic Properties and Reaction Kinetics of Ni0.5Co0.5Fe2O4 Reduction in Hydrogen Atmosphere

Title
The Effect of Temperature on Microstructure, Magnetic Properties and Reaction Kinetics of Ni0.5Co0.5Fe2O4 Reduction in Hydrogen Atmosphere
Author
박종진
Keywords
nickel cobalt ferrite; H-2-reduction; nanocrystallites; iron nickel cobalt alloy; reduction kinetics
Issue Date
2008-04
Publisher
JAPAN INST METALS
Citation
MATERIALS TRANSACTIONS, v. 49, No. 4, Page. 860-868
Abstract
Nickel cobalt ferrite (Ni0.5Co0.5Fe2O4) powder was prepared through the ceramic route by calcination of a stoichiometric mixture of nickel oxide, cobalt oxide and iron oxide at 1100 and 1200 degrees C. The produced powders of Ni0.5Co0.5Fe2O4 were isothermally reduced in pure hydrogen at 800-1100 degrees C. Based on thermogravimetric analysis, the reduction behavior of nickel cobalt ferrite and the kinetics reaction mechanism were studied. The initial ferrite powder and the various reduction products were characterized by XRD, pore size, SEM, VSM and reflected light microscope to reveal the effect of hydrogen reduction on composition, microstructure and magnetic properties of produced Fe-Ni-Co alloy. Microstructure of partially and completely reduced samples was studied and the activation energy values were calculated from Arrhenius equation. The approved mathematical formulations for the gas solid reaction were applied and it was found that the initial reaction stages are controlled by the combined gaseous diffusion and interfacial chemical reaction mechanisms with high contribution to gas diffusion while the final reaction stages is controlled by chemical reaction mechanism. Complete reduction of Ni0.5Co0.5Fe2O4 was achieved with synthesis of nanocrystalline (18-20 nm) Fe-Ni-Co alloy.
URI
https://www.jstage.jst.go.jp/article/matertrans/49/4/49_MER2007268/_article/-char/ja/https://repository.hanyang.ac.kr/handle/20.500.11754/104479
ISSN
1345-9678
DOI
10.2320/matertrans.MER20072681
Appears in Collections:
COLLEGE OF ENGINEERING SCIENCES[E](공학대학) > MATERIALS SCIENCE AND CHEMICAL ENGINEERING(재료화학공학과) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE