Determination of the continuous cooling transformation diagram of a high strength low alloyed steel
- Title
- Determination of the continuous cooling transformation diagram of a high strength low alloyed steel
- Author
- 이경종
- Keywords
- alloys; thermomechanical processing; phase transformation; dilatometry; CCT
- Issue Date
- 2016-11
- Publisher
- KOREAN INST METALS MATERIALS
- Citation
- METALS AND MATERIALS INTERNATIONAL, v. 22, NO. 6, Page. 949-955
- Abstract
- The continuous cooling transformation diagram of a high strength low alloyed steel was determined by a dilatometer and microscopic analysis (OM, SEM) as well as thermodynamic analysis. As expected, Widmanstatten ferrite, bainite and martensite coexisted for most cooling rates, which made it difficult to determine the transformation kinetics of individual phases. However, peaks were clearly observed in the dilatometric curves. By overlapping the curves, which were determined using various cooling rates, peaks were separated and the peak rate temperatures, as well as the temperature at the start of transformation (5%) and the end of transformation (95%) of an individual phase, were determined. A SEM analysis was also conducted to identify which phase existed and to quantify the volume fraction of each phase. It was confirmed that the additional curve analysis described the transformation behavior more precisely than the conventional continuous cooling transformation diagram, as determined by the volume measured from the microstructure analysis.
- URI
- https://link.springer.com/article/10.1007%2Fs12540-016-6269-1https://repository.hanyang.ac.kr/handle/20.500.11754/101135
- ISSN
- 2005-4149; 1598-9623
- DOI
- 10.1007/s12540-016-6269-1
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > MATERIALS SCIENCE AND ENGINEERING(신소재공학부) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML