TY - JOUR AU - 노삼영 DA - 2007/09 PY - 2007 UR - http://www.dbpia.co.kr/journal/articleDetail?nodeId=NODE00881677&language=ko_KR UR - https://repository.hanyang.ac.kr/handle/20.500.11754/106970 AB - The formation of cracks in the reinforced concrete member is generally prerequisite. Therefore structural building codes suggest prediction formulas and limits of crack width for the durability and the serviceability of structures in which steel corrosion can be initiated through the cracks. The crack behavior of a reinforced tension member has been theoretically more or less mastered, although the accuracy of the prediction formulas for crack width suggested building codes is questionable. Additionally influence of steel corrosion indicated by concrete cracks on the crack width have not been referred. The aim of this study is the analysis of the crack behavior of a crack element between two cracks under steel corrosion after the crack formation. For this purpose a bond-slip relation was numerically modelled based on steel corrosion test results by other researchers. With the bond model and other effects due to the steel corrosion, the crack element was numerically analyzed. As results, bond stress, slip, steel stress and crack width in a crack element could be obtained in dependence on the corrosion duration of reinforced concrete structural members. PB - 대한건축학회 KW - 부착응력 KW - 슬립 KW - 균열폭 KW - 부식모델 KW - 탄산화 KW - 환경조건 KW - Bond Stress KW - Slip KW - Crack Width KW - Corrosion Model KW - Carbonation KW - Environmental Condition TI - 균열발생 후 철근부식을 고려한 철근콘크리트 인장부재의 균열거동 TT - Crack Behavior of Reinforced Concrete Tension Member under Steel Corrosion after Cracking T2 - 대한건축학회논문집 ER -