Fabrication of a semi-transparent flexible humidity sensor using kinetically sprayed cupric oxide film

Title
Fabrication of a semi-transparent flexible humidity sensor using kinetically sprayed cupric oxide film
Author
이선영
Keywords
Cupric oxide; Flexible sensor; Humidity; Kinetic spray
Issue Date
2018-11
Publisher
ELSEVIER SCIENCE SA
Citation
SENSORS AND ACTUATORS B-CHEMICAL, v. 274, Page. 331-337
Abstract
In this study, a cupric oxide (CuO) flexible humidity sensor was fabricated using a kinetic spray process. After deposition of a 200-nm-thick Cu film, the as-deposited Cu layer was annealed at 250 degrees C, a relatively low temperature, in air conditions to create a CuO layer. N-type CuO (carrier concentration: -23.08x10(14) cm(-3)) formed after reacting with oxygen during the annealing process in air via oxygen vacancy formation. The semi-transparent properties of the CuO film were characterized by measuring visible light transmittance. Stable sensing signals of 0.16-0.18 were obtained after the 1000th bending test. Scanning electron microscopy was used to examine the surface morphology of the CuO layer after the bending test; despite the presence of a few microcracks, delamination was not observed. Thus, a CuO-based humidity sensor was successfully fabricated through simple particle spray deposition and low-temperature annealing processes; the sensor maintained its performance under repeated bending stress (up to 1000 cycles).
URI
https://www.sciencedirect.com/science/article/pii/S0925400518313753http://repository.hanyang.ac.kr/handle/20.500.11754/98770
ISSN
0925-4005
DOI
10.1016/j.snb.2018.07.127
Appears in Collections:
COLLEGE OF ENGINEERING SCIENCES[E](공학대학) > MATERIALS SCIENCE AND CHEMICAL ENGINEERING(재료화학공학과) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE