Distribution Behavior of Aluminum and Titanium Between Nickel-Based Alloys and Molten Slags in the Electro Slag Remelting (ESR) Process

Abstract

The equilibrium reaction between Ni alloys and CaO-Al2O3-CaF2-TiO2 system electroslag remelting (ESR) slags was investigated in the temperature range of 1773 K to 1873 K (1500 A degrees C to 1600 A degrees C) at p(O-2) = 10(-16) atm in order to obtain the optimized composition of the slags for producing Ni alloys with various Al and Ti ratios. In addition, the temperature dependence of the reaction equilibria between the ESR slags and Ni alloys was also evaluated. The stable ionic species of titanium in the ESR slag under the present experimental conditions was experimentally confirmed to be mainly Ti4+ (i.e., TiO2) by X-ray photoelectron spectroscopy analysis of the quenched samples. The activity-composition relationship of TiO2 and Al2O3 in the ESR slag was determined as a function of the Al/Ti ratio of the alloys and the CaF2 content of the slags in conjunction with the activity ratio of Al to Ti in the alloys calculated from the FactSage(TM) 7.0 software. The temperature dependence of the activity-composition relationship of TiO2 and Al2O3 in the slag showed good linear correlations, and the equilibrium content ratio of TiO2 to Al2O3 at a fixed activity ratio increased with increasing temperature, which was expected based on the standard enthalpy change of the reaction. Thus, higher amounts of TiO2 should be added at higher operation temperatures in the ESR process. A 120 kg scale pilot ESR test (2000 A and 16 V) was performed to produce a commercial grade Ni-based superalloy based on the activity-composition relationship of the slag components obtained in the present study. Consequently, the contents of Al and Ti in the solidified ESR ingot were nearly the same as that of the original electrode throughout the entire length (280 mm) after the ESR process. (C) The Minerals, Metals Materials Society and ASM International 2017