An experimental study on the characteristics of chemically synthesized nano-cement for carbon dioxide reduction

Title
An experimental study on the characteristics of chemically synthesized nano-cement for carbon dioxide reduction
Author
조병완
Keywords
CO(2) reduction; Chemical synthesis; Alkali activation; Compressive strength; Highly functional construction material
Issue Date
2011-06
Publisher
Stafa-Zurich; Trans Tech Publications
Citation
Advanced Materials Research, 2011, 148-149(2), P.1717-1721
Abstract
Cement is becoming a principal factor in air pollution because of the creation of CO2 during its manufacturing. The exhaustion of the natural resources needed for Portland cement production is also an issue. Therefore, a substitute material for this type of cement is needed. Nano-scale materials are of great interest due to their unique optical, electrical, and magnetic properties. These properties are strongly dependent on the sizes and shapes of the particles, and, therefore, it is important to be able to develop the construction part which retains the excellent properties of the nano-sized material. The purpose of this study was to synthesize nano-powder as a substitute for cement using a chemical method. This study investigated the compressive strengths of concretes with various compositions. Specimens were tested for compressive strength three, seven, 14, and 28 days after manufacture. In the results of this study, the medium-sized (50% by weight) nano-cement particles created via chemical synthesis were less than 168 nm in size, and the compressive strength of the mortar prepared using these nanoparticles was 53.9 MPa
URI
https://www.scientific.net/AMR.148-149.1717http://hdl.handle.net/20.500.11754/66725
ISSN
1022-6680
DOI
10.4028/www.scientific.net/AMR.148-149.1717
Appears in Collections:
COLLEGE OF ENGINEERING[S](공과대학) > CIVIL AND ENVIRONMENTAL ENGINEERING(건설환경공학과) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE