Behaviour of CaO coating of gas atomized Mg powders using mechanical milling process
- Title
- Behaviour of CaO coating of gas atomized Mg powders using mechanical milling process
- Author
- 김영도
- Keywords
- Mg powder; Gas atomization; Mechanical milling; Desulfurization; CaO coating
- Issue Date
- 2011-06
- Publisher
- Elsevier Science B.V., Amsterdam.
- Citation
- JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509, P.S503-S506
- Abstract
- In order to synthesize a thermally stable Mg powder as a desulfurizer of iron, pure Mg was gas atomized to powders and coated by CaO powders, to produce a thermally stable desulfurizer using a mechanical milling process. Since the effect of desulfurization is dependent on the degree of surface modification, coating behaviours such as the size, morphology and layer thickness were investigated as a function of milling condition. As the milling conducted from 10 min to 30 min, 1 h, 3 h, 6 h, 12 h, CaO particles began to stick on the surface of Mg powders. The layer of CaO formed from 1 h milling was about 17 mu m thick and gradually thickened to be 28 mu m, 32 mu m and 37 mu m with increasing the milling time to 3 h, 6 h and 12 h, respectively. The shape of coated powder became more spherical after 1 h milling, being mostly spherical after 6 h. Desulfurization rate and uniformity were evaluated for the various thickness of the coating layer. (C) 2011 Elsevier B.V. All rights reserved.
- URI
- https://www.sciencedirect.com/science/article/pii/S0925838811004129?via%3Dihubhttp://hdl.handle.net/20.500.11754/66719
- ISSN
- 0925-8388
- DOI
- 10.1016/j.jallcom.2011.02.078
- Appears in Collections:
- COLLEGE OF ENGINEERING[S](공과대학) > MATERIALS SCIENCE AND ENGINEERING(신소재공학부) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML