A new synthetic route to hollow Co3O4 octahedra for supercapacitor applications

Abstract

Co3O4 hollow octahedra were successfully synthesized via a facile one-step solvothermal route. Time-resolved electron microscopy and X-ray diffraction analyses revealed that the Co3O4 hollow octahedra were formed through the self-assembly of primary nanocrystals followed by subsequent Ostwald ripening. Subtle control over the reaction conditions led to different morphologies (hexagonal plates and nanocubes) and crystal structures (beta-Co(OH)(2)-Co3O4 composite). The unique hollow nanostructure rendered our Co3O4 potentially useful for charge-storage applications. To prove its usefulness, the pseudocapacitive performance of the Co3O4 hollow octahedra as a supercapacitor electrode was evaluated and exhibited a charge storage capacity of 192 F g(-1) with good long-term cyclability.코 3 O 4 움푹한 옥타헤드라는 성공적으로 쉽게 얻을 수 있는 원 스텝 용매열 경로를 통해 합성되었다. 코 3 O 4 움푹한 옥타헤드라가 연속적 오스트발트 숙성이 이어진 중요한 나노결정의 자동조립을 통하여 형성되었다고 시간 분해된 전자 현미경 검사와 X-선 회절 분석은 밝혔다. 반응 조건에 대한 미묘한 조절은 다른 형태학 (육각 플레이트와 나노큐브)과 결정 구조로 이어졌고 (β-Co (오) 2 ? 코 3 O 4 복합체). 유일한 움푹한 나노구조는 충전 저장 응용을 위해 우리의 코 3 O에게 잠재적으로 유용한 4를 제공했다. 그것의 유용성을 입증하기 위해, 슈퍼커패시터 전극으로서의 코 3 O 4 할로우 옥타헤드라의 모조 전기 용량 성능은 평가받았고, 좋은 장기 순환성으로 192 F g ?1의 전하 저장 용량을 나타냈다. 새로운 용액 열 분해법을 통하여 합성된 그래픽 이론적 움푹한 코 3 O 4 옥타헤드라가 좋은 장기 순환성으로 192 F g ?1의 전하 저장 용량을 나타냈다.