Effect of carbide size and spacing on the fretting wear behavior of Inconel 690 SG tube mated with SUS 409

Title
Effect of carbide size and spacing on the fretting wear behavior of Inconel 690 SG tube mated with SUS 409
Author
김선진
Keywords
Inconel 690; Fretting wear; Steam generator; Nuclear power plant; Carbide; Coarsening
Issue Date
2015-09
Publisher
ELSEVIER SCIENCE SA
Citation
WEAR, v. 338, Page. 252-257
Abstract
The effect of carbide size and spacing on the fretting wear resistance of Inconel 690 steam generator (SG) tube mated with SUS 409 was investigated in this study. Based on previous materials tribology research, we reasoned that increasing carbide size and spacing would increase the wear resistance of the Inconel 690. Experiments were performed to test this hypothesis. Commercialized Inconel 690 tube with mean carbide length, thickness and spacing of 0.29, 0.10, and 0.59 mu m, respectively, was used for the wear test. Carbide length, thickness, and spacing increased to 0.36, 0.15, and 0.68 mu m, respectively after heat treatment at 450 degrees C for 16 h without changes in carbide volume fraction, grain size or hardness. The results of the wear test showed that at the amplitude of 25 mu m, wear coefficient did not change due to stick phenomenon. At the amplitude of 50 mu m-150 mu m, wear coefficient decreased about 50%. At the amplitude of 300 mu m, the wear coefficient decreased from 2.7 X 10(-13) m(3)/Nm to 2.0 x 10(-13) m(3)/Nm due to increase in carbide size and spacing. (C) 2015 Elsevier B.V. All rights reserved.
URI
http://www.sciencedirect.com/science/article/pii/S0043164815003440http://hdl.handle.net/20.500.11754/27493
ISSN
0043-1648; 1873-2577
DOI
10.1016/j.wear.2015.06.012
Appears in Collections:
COLLEGE OF ENGINEERING[S](공과대학) > MATERIALS SCIENCE AND ENGINEERING(신소재공학부) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE