Improvement in the pitting resistance of Inconel-600 by nitrogen ions implantation

Title
Improvement in the pitting resistance of Inconel-600 by nitrogen ions implantation
Authors
김용수
Keywords
STRESS-CORROSION CRACKING; CHLORIDE SOLUTIONS; OW-TEMPERATURE; ALLOY 600; SUPERALLOYS; BEHAVIOR; KINETICS; STEEL; WATER
Issue Date
2015-07
Publisher
MAIK NAUKA/INTERPERIODICA/SPRINGER
Citation
PROTECTION OF METALS AND PHYSICAL CHEMISTRY OF SURFACES, v. 51, no. 3, Page. 481-485
Abstract
The surface of Ni-Cr-Fe (Inconel-600) alloy was modified by implanting 500 keV nitrogen ions at room temperature using pelletron accelerator to dose of 1.87 x 10(14) ions/cm(2). X-ray diffraction analysis of the ions implanted samples indicated the formation of Cr2N phase. Electrochemical testing of Inconel-600 alloy before and after the ions implantation was conducted using potentiodynamic tafel scan, potentiodynamic anodic polarization and electrochemical impedance spectroscopy techniques in an acidic saline solution. The higher anodic polarization slope (beta(a)), low cathodic polarization slope (beta(c)) and decrease in corrosion current density after ions implantation were attributed to the modification of passive film by the nitrogen ions. The scanning electron microscopy and electrochemical analyses of the ions implanted samples revealed an improvement in the pitting resistance of the alloy.
URI
http://link.springer.com/article/10.1134/S207020511503003Xhttp://hdl.handle.net/20.500.11754/26186
ISSN
2070-2051; 2070-206X
DOI
http://dx.doi.org/10.1134/S207020511503003X
Appears in Collections:
COLLEGE OF ENGINEERING[S](공과대학) > NUCLEAR ENGINEERING(원자력공학과) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE