Effect of microstructural evolution on wettability and tribological behavior of TiO2 nanotubular arrays coated on Ti-6Al-4V

Title
Effect of microstructural evolution on wettability and tribological behavior of TiO2 nanotubular arrays coated on Ti-6Al-4V
Authors
Zal Nezhad, Erfan
Keywords
Ti-6Al-4V; TiO2 nanotube; Tribological behavior; Wettability; Anodization
Issue Date
2015-03
Publisher
ELSEVIER SCI LTD
Citation
CERAMICS INTERNATIONAL, v. 41, NO 6, Page. 7952-7962
Abstract
Self-organized TiO2 nanotubular arrays were fabricated by electrochemical anodization of Ti-6Al-4V plates in an NH4F/H3PO4 electrolyte. The effect of microstructural evolutions on the wettability and tribological behavior of the TiO2 nanotubes was investigated. Based on the XRD profiles of the fabricated material, the characteristic TiO2 peaks were not recognized after anodization; however, highly crystalline TiO2 (anatase and rutile) was formed due to crystallization during annealing at 500 degrees C for 1.5 h. The nanotube arrays were converted entirely to rutile at 700 degrees C. From a microstructure point of view, a highly ordered nanotube structure was achieved when the specimen was annealed at 500 degrees C, with a length of 0.72 mu m and a pore diameter of 72 nm. Further increasing the annealing temperature to 700 degrees C resulted in the complete collapse of the tubular structure. The results indicate that the improved wettability of the anodized specimens was due to the combination of the effects of both the surface oxide layer and the increased surface roughness achieved after anodization. Moreover, the wear resistance and wettability of the sample annealed 500 degrees C were improved due to the high hardness (435 HV) and low coefficient of friction (0.133-168) of the highly crystalline structure of the TiO2 nanotubes. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
URI
http://www.sciencedirect.com/science/article/pii/S0272884215003776http://hdl.handle.net/20.500.11754/22911
ISSN
0272-8842; 1873-3956
DOI
http://dx.doi.org/10.1016/j.ceramint.2015.02.136
Appears in Collections:
COLLEGE OF ENGINEERING[S](공과대학) > MECHANICAL ENGINEERING(기계공학부) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE