Characterization of recycled polyethylene terephthalates and polyethylene terephthalate-nylon6 blend knitted fabrics

Title
Characterization of recycled polyethylene terephthalates and polyethylene terephthalate-nylon6 blend knitted fabrics
Author
김성훈
Keywords
mechanically recycled polyethylene terephthalate; chemically recycled polyethylene terephthalate; recycled polyethylene terephthalate-nylon6 blend
Issue Date
2015-03
Publisher
SAGE PUBLICATIONS LTD
Citation
TEXTILE RESEARCH JOURNAL, v. 85, Page. 337-345
Abstract
"For environmental conservation, post-consumer polyethylene terephthalate (PET) bottles are recycled using methods ranging from mechanical recycling to various chemical recycling processes. In this study, the characterization of recycled PETs and PET-nylon6 blend knitted fabrics, and virgin PET knitted fabric, was carried out with the aim of broadening the application of recycled PET fabrics. The tensile strength values of mechanically and chemically recycled PET knitted fabrics were similar to those of virgin PET knitted fabric. The elongation of recycled PET-nylon6 blend knitted fabric was the best. Both virgin and recycled PET knitted fabrics had excellent pilling resistance. Based on the drape ratio, the recycled PET-nylon6 blend knitted fabric was more flexible than other samples. The warm/cool feeling (Q(max)), compressional and surface properties were measured using the Kawabata evaluation system for fabrics (KES-FB system). The compressional properties of mechanically recycled PET knitted fabric were similar to those of virgin PET knitted fabric. The recycled PET-nylon6 blend knitted fabric showed the smoothest appearance and coolest feeling among the four samples. Moisture regain and moisture permeability were the best in recycled PET-nylon6 blend knitted fabric. However, the wickability of mechanically recycled PET knitted fabric was better than other recycled PET knitted fabrics."
URI
http://trj.sagepub.com/content/85/4/337.shorthttp://hdl.handle.net/20.500.11754/22817
ISSN
0040-5175; 1746-7748
DOI
10.1177/0040517514547207
Appears in Collections:
COLLEGE OF ENGINEERING[S](공과대학) > ORGANIC AND NANO ENGINEERING(유기나노공학과) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE