유화아스팔트/폴리우레탄 혼합물을 이용한 건축용 방수멤브레인 제조 및 특성

Abstract

A waterproof membrane which can be used for constructions was prepared by the blend of emulsified asphalt and polyurethane prepolymer. Effects of composition and mixing ratio of urethane prepolymer to which various ISOYNATEs(NCO% 3.5∼8.7), which can be mixed with emulsified asphalt with a solid content of 70%, viscosity of 490cps, and pH10, were applied. As a resul, it was confirmed that the polyurethane prepolymer prepared by applying TDI and IPDI at a ratio of 1:1 when mixing emulsified asphalt and polyurethane prepolymer having each NCO% showed stable tensile strength, elongation, and tear strength. When IPDI (isophorone diisocyanate), which has a hydrophilic group with excellent compatibility with emulsified asphalt, is applied at a certain ratio, it was confirmed that the compatibility and physical properties of emulsified asphalt and urethane complemented each other. Based on the above results, it is judged that it can be applied to various membranes by confirming the compatibility and physical properties of asphalt and urethane prepolymer.| 본 연구에서 건축용 콘크리트 구조물의 누수를 방지하기 위하여 아스팔트의 장점과 우레탄의 장점을 결합시켜 높은 신장률과 강도를 가지는 건축용 방수 멤프레인의 제조 및 특성에 관하여 연구하였다. 이를 위하여 스트레이트 아스팔트를 유화시킨 유화아스팔트와 혼합이 가능한 우레탄 프리폴리머의 조성 및 혼합비율 조정을 통한 실험으로 상용성 및 물성을 확인하였다. 물성실험 결과 유화아스팔트와 TDI 및 IPDI를 1:1로 적용하여 제조된 폴리우레탄 프리폴리머가 혼합된 멤브레인이 안정된 인장강도와 신장율, 인열강도를 나타내는 것을 확인 하였다. 유화아스팔트와 상용성이 우수한 친수성기를 가진 IPDI(이소포론 디이소시아네이트)를 일정비율 적용시 유화아스팔트와 우레탄의 상용성 및 물성을 상호 보완한 물성을 나타내는 것을 확인하였다. 이와 같이 아스팔트와 우레탄 프리폴리머의 상용성 및 물성 확인으로 다양한 멤브레인에 적용 가능할 수 있을 것으로 판단된다.