Supreme performance of zinc oxynitride thin film transistors via systematic control of the photo-thermal activation process

Title
Supreme performance of zinc oxynitride thin film transistors via systematic control of the photo-thermal activation process
Author
박진성
Keywords
EXCEEDING 50 CM(2)/VS
Issue Date
2018-04
Publisher
ROYAL SOC CHEMISTRY
Citation
JOURNAL OF MATERIALS CHEMISTRY C, v. 6, no. 19, page. 5171-5175
Abstract
Zinc oxynitride (ZnON) is a relatively novel class of material, often regarded as a promising alternative to oxide semiconductors, owing to its relatively high electron mobility and low concentration of oxygen-related defects that affect the device reliability. In the present study, thermal annealing of ZnON for thin film transistor (TFT) applications is performed in conjunction with a source of ultraviolet (UV) radiation, as an attempt to lower the heat treatment temperature. The oxygen radicals and ozone produced in this process appear to oxidize the ZnON surface. As the annealing temperature increases in the presence of UV light, chemically stable ZnO and non-stoichiometric ZnxNy bonds are formed without significant change in the oxygen/nitrogen ratio within the film. Such a phenomenon is accompanied by a slight reduction in the field effect mobility and device stability under positive bias stress, however under optimized photo-thermal annealing conditions, ZnON TFTs fabricated at a relatively low annealing temperature (150 degrees C) exhibit high field effect mobility values exceeding 50 cm(2) V-1 s(-1) and reasonable reliability, as examined under positive bias stress conditions.
URI
https://pubs.rsc.org/en/content/articlelanding/2018/TC/C8TC01064A#!divAbstracthttp://repository.hanyang.ac.kr/handle/20.500.11754/118275
ISSN
2050-7526; 2050-7534
DOI
10.1039/c8tc01064a
Appears in Collections:
COLLEGE OF ENGINEERING[S](공과대학) > MATERIALS SCIENCE AND ENGINEERING(신소재공학부) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE