Ten-gram-scale preparation of PTMS-based monodisperse ORMOSIL nano-and microparticles and conversion to silica particles

Title
Ten-gram-scale preparation of PTMS-based monodisperse ORMOSIL nano-and microparticles and conversion to silica particles
Author
구상만
Keywords
Phenyltrimethoxysilane; ORMOSIL; Nanoparticle; Microparticle; Self-emulsion process; Conversion to silica
Issue Date
2018-03
Publisher
SPRINGER
Citation
JOURNAL OF NANOPARTICLE RESEARCH, v. 20, no. 3, Article no. 73
Abstract
Monodisperse organically modified silica (ORMOSIL) particles, with an average diameter ranging from 550 nm to 4.2 mu m, were prepared at low temperature at a scale of about 10 g/batch by a simple one-step self-emulsion process. The reaction mixture was composed only of water, phenyltrimethoxysilane (PTMS), and a base catalyst, without any surfactants. The size control of the particles and the monodispersity of resultant particles were achieved through the controlled supply of hydrolyzed PTMS monomer molecules, which was enabled by manipulating the reaction parameters, such as monomer concentration, type and amount of base catalyst, stirring rate, and reaction temperature. PTMS-based ORMOSIL particles were converted into silica particles by employing either a wet chemical reaction with an oleum-sulfuric acid mixture or thermal treatment above 650 degrees C. Complete removal of organic groups from the ORMOSIL particles was achieved by the thermal treatment while similar to 74% removal was done by the chemical process used.
URI
https://link.springer.com/article/10.1007%2Fs11051-018-4186-6http://repository.hanyang.ac.kr/handle/20.500.11754/117753
ISSN
1388-0764; 1572-896X
DOI
10.1007/s11051-018-4186-6
Appears in Collections:
COLLEGE OF ENGINEERING[S](공과대학) > CHEMICAL ENGINEERING(화학공학과) > Articles
Files in This Item:
There are no files associated with this item.
Export
RIS (EndNote)
XLS (Excel)
XML


qrcode

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.

BROWSE