Service Life Estimation of Concrete Structures Reinforced with Cr-bearing Rebar under Macrocell Corrosion Conditions Induced by Cracking in Cover Concrete
- Title
- Service Life Estimation of Concrete Structures Reinforced with Cr-bearing Rebar under Macrocell Corrosion Conditions Induced by Cracking in Cover Concrete
- Author
- 태성호
- Keywords
- Cr-bearing rebar; service life estimation; macrocell corrosion; crack
- Issue Date
- 2007-06
- Publisher
- IRON STEEL INST JAPAN KEIDANREN KAIKAN
- Citation
- ISIJ INTERNATIONAL, v. 47, No. 6, Page. 875-882
- Abstract
- Cracked concrete members reinforced with Cr-bearing rebars were assumed for the purpose of developing Cr-bearing rebars having the required corrosion resistance in macrocell corrosion environments induced by cracking in cover concrete. The service life of concrete structures reinforced with Cr-bearing rebars was then estimated based on a macrocell corrosion rate model, and their Cr content to achieve a service life of 100 years was calculated. As a result, the service life of concrete reinforced with Cr-bearing rebars was found to increase as their Cr content increased regardless of the corrosive environment type, The calculation also revealed that Cr contents of 16% or more and 13% or more would lead to a service life of over 100 years in harsh and moderate chloride attack zones, respectively. In a carbonation zone, the Cr content to achieve a service life of over 100 years was calculated to be 9% or more.
- URI
- https://www.jstage.jst.go.jp/article/isijinternational/47/6/47_6_875/_article/-char/ja/https://repository.hanyang.ac.kr/handle/20.500.11754/106625
- ISSN
- 0915-1559; 1347-5460
- DOI
- 10.2355/isijinternational.47.875
- Appears in Collections:
- COLLEGE OF ENGINEERING SCIENCES[E](공학대학) > ARCHITECTURE(건축학부) > Articles
- Files in This Item:
There are no files associated with this item.
- Export
- RIS (EndNote)
- XLS (Excel)
- XML